Quick Details

  • Standard: AiSi, ASTM, bs, DIN, GB, JIS
  • Grade: alloy steel
  • Place of Origin: China
  • Brand Name: CF Steel
  • Model Number: 1.2738/P20+Ni/ 3Cr2NiMnMo/718H
  • Type: Steel Plate
  • Technique: Hot Rolled
  • Surface Treatment: Black/milling/machined, Black/Peeling/Polishing/Machined
  • Application: plastic mold steel plate
  • Special Use: Mold steel
  • Width: 1600-2200mm
  • Length: 2000-8000mm
  • Shape: Round Bar or Flat Steel or Forged Block
  • Heat Treatment: Annealed / Q+T
  • Test: Ut 100% / SGS
  • Certificate: ISO / Mill Certificate
  • Hardness: 33-37HRC
  • Thickness: 21-300mm

Packaging & Delivery

Packaging Details Export Standard Packing or Customers'demand
Port Shenzhen

 

High Quality Forged 1.2738 Mold Steel Plate Pre-hardened HRC 30-36

 

 

1.2738 is a pre-hardened Plastic Mold Steel.

 

 

Equivalent grades

 

GBDINAISIASSAB
3Cr2NiMnMo1.2738P20+Ni718

 

 

Chemical Composition(%)

 

CSiMnPSCrMoNi
0.28-0.400.20-0.800.60-1.00≤0.03≤0.0151.40-2.000.30-0.550.80-1.20

 

 

Hardness: Pre-hardened 33-37 HRC

 

 

Applications

 

1) Suitable for molds with high gloss.
2) After the mold steel nitride surface hardness can reach 650 ~ 700HV, the number of products can reach more than 1 million die.

 

 

Delivery Time


Stock items 15-20 days; customized items 30-50 days.

 

 

Packing: Standard export packing; customers' special requests are accepted

 

 

Material properties


Local heating with oxyacetylene flame can be used to achieve partial quench hardening: the hardened area will be hardened, heated to light red (850-950 ° C) and then cooled in air.

 

In order to prevent the mold from cracking due to excessive stress, tempering should be carried out at 150 ~ 200 ℃ and the surface hardness can reach 45 ~ 50HRC after flame hardening.

 

Note that in the flame hardening treatment, the mold should be 150-200 ℃: preheating to prevent mold cracking. Nitriding mold can get high hardness of the surface organization, nitrided surface smooth and dense, with good corrosion resistance, is conducive to product touch and improve production efficiency.

 

 

Supply status


Pre-hardened and tempered, hardness of a 320HBW, 320 a 350HBW

 

 

Thermal processing specifications


The starting temperature of 1050 ℃, the termination temperature of 850 ℃, furnace cooling.

 

 

Quenching norms


Preheat temperature 500 a 600`C, insulation 2 a 4h, then rose to 850 a 880 ℃, insulation ≥ 2h, the oil cooled to 50 ~ 100 ℃, and then air-cooled, hardness 50 a 53HRC, quench cracking in order to prevent tempering immediately deal with.

 

 

Quality Condition


1. Both end of each bar must be cut as require
2. Ladle furnanced and vacuum de-gassed
3. Show heat No. on each bar
4. Surface condition the surface of the hot rolled square bar shall befree cracks, scar and wrinkles that affect the use of the billets. In case there is the above-mentioned defect, it shall be remove.
5. The mill test certificate shall show the chemical composition, and it is guaranteed that the chemical composition shall be within the limit stipulated in the contract.

 

 

About US

 

Guangzhou Changfeng Steel Co., Ltd is a mould steel stockist, we have our own factory and trading company. Our main steels are carbon tool steel, plastic mold steel, hot work tool steel, cold work tool steel, alloy steel for mechanical, etc. All material are with high quality and competitive price.

 

We have different grades steel with different sizes in stocks all the time, shipment can be arranged fast. For customize items, we can also arranged the shipment within 30-50 days after receiving your prepayment or firm order.

 

We are here waiting for a cooperation chance between us, contact us and you will have one more loyal mold steel supplier!

 

 